EOS
PA 2220 HighReuse
SLS · PA12 · White
EOS PA 2220 HighReuse is a highly efficient polyamide 12 that serves a wide range of applications thanks to a balanced property profile. It allows a 70% powder reuse rate, which reduces material waste and lowers the cost per part.
48 MPa dry
Tensile Strength
1800 MPa dry
Tensile Modulus
X: 10% dry/14% conditioned
Elongation at Break
64°C (X)
Heat Deflection Temperature
Finish and colour of the material as printed
Why choose PA 2220 HighReuse?Why this material
Reduces material waste and lowers the cost per part
A balanced property profile
A versatile material in white
Easy to dye with advanced finishing solutions
Technical propertiesVerified figures only
48 MPa dry
45 MPa conditioned, in X,Y · 48 MPa dry / 42 MPa conditioned, in Z (ISO 527-1/-2)
Tensile Strength
1800 MPa dry
1500 MPa conditioned, in X,Y · 1800 MPa dry / 1300 MPa conditioned, in Z (ISO 527-1/-2)
Tensile Modulus
X: 10% dry/14% conditioned
Y: 9%/15% · Z: 8%/12% (ISO 527-1/-2)
Elongation at Break
64°C (X)
57°C (Z) at 1.80 MPa (ISO 75-1/-2)
Heat Deflection Temperature
79 Shore D in X
dry (ISO 7619-1)
Shore Hardness
0.99 g/cm³
(DIN EN ISO 1183)
Density
White
Natural Color
Typical applicationsWhat it is used for
Eyewear
Brackets
Jigs and fixtures
Spare parts
Functional prototypes
Compatible printersSystems that run this material
EOS P3 NEXT
DocumentsTechnical data sheet
Technical Data Sheet
Download the Technical Data SheetMaterial characteristicsAppearance and classification
- 70% reusability
- balanced profile
- easy to color
Similar materials
Other SLS materials from a related family or with similar properties
Need help choosing a material?
Our team will help you match the project, the technology and the right material.