Stratasys
High Yield PA11
SAF · PA11
Stratasys High Yield PA11 is produced in SAF technology on the H350 printer, giving industrial-grade plastic parts for high-volume demand. The material is 100% based on sustainable castor oil, and allows high nesting density while holding part properties consistent throughout the build volume.
51 ± 2.2 MPa (orientation XZ/YZ)
Tensile Strength
1529 ± 76 MPa (XZ/YZ)
Tensile Modulus
30 ± 5.6% (XZ/YZ)
Elongation at Break
185°C at 0.45 MPa
Heat Deflection Temperature
Finish and colour of the material as printed
Why choose High Yield PA11?Why this material
Greater flexibility and impact resistance than PA12
Suited to a wider range of industrial applications
An environmentally friendly, bio-based composition from castor oil
Consistent properties throughout the build volume
Technical propertiesVerified figures only
51 ± 2.2 MPa (orientation XZ/YZ)
47 ± 4.4 MPa (orientation ZX), ASTM D638-14
Tensile Strength
1529 ± 76 MPa (XZ/YZ)
1609 ± 99 MPa (ZX), ASTM D638-14
Tensile Modulus
30 ± 5.6% (XZ/YZ)
11 ± 4.8% (ZX), ASTM D638-14
Elongation at Break
185°C at 0.45 MPa
47°C at 1.82 MPa, ASTM D648
Heat Deflection Temperature
UL94 HB Pass (2013)
Flame Rating
Typical applicationsWhat it is used for
Orthotics – durable and flexible, suited to custom orthotic devices with high impact resistance
Automotive – lightweight, durable parts for high-load components
Consumer products – an environmentally friendly, durable material for consumer goods and electronics
A wide range of industrial applications and volume production of end-use parts
Compatible printersSystems that run this material
H350
DocumentsTechnical data sheet
Technical Data Sheet
Download the Technical Data SheetMaterial characteristicsAppearance and classification
- Bio-based
- flexible
- impact resistant
Need help choosing a material?
Our team will help you match the project, the technology and the right material.